Natural zeolite block for improving water quality and method for manufacturing same

ABSTRACT

A natural zeolite block for improving water quality that is capable of being built in rivers, streams, and reservoirs having point and non-point pollutant sources to purify the water polluted by pollutants, to remove the eutrophication in the water to prevent the occurrence of green and red tides, and to consistently purify heavy metals and all kinds of harmful substances flowing into the water and to a method for manufacturing the same.

CROSS REFERENCE TO RELATED APPLICATION OF THE INVENTION

This application is a divisional of U.S. application Ser. No. 17/847,346filed Jun. 23, 2022, which claims the benefit of Korean PatentApplication No. 10-2021-0187935 filed in the Korean IntellectualProperty Office on Dec. 27, 2021, the entire contents of which areincorporated herein by reference.

BACKGROUND OF THE INVENTION Field of the Invention

The present invention relates to a natural zeolite block for improvingwater quality that is capable of being built in rivers, streams, andreservoirs having point and non-point pollutant sources to purify thewater polluted by pollutants, to remove the eutrophication in the waterto prevent the occurrence of green and red tides, and to consistentlypurify heavy metals and all kinds of harmful substances flowing into thewater and to a method for manufacturing the same.

A zeolite as a natural mineral is adopted to achieve objects of thepresent invention.

The natural zeolite is a microporous mineral that occurs naturally bythe solidification of volcanic lava, and it is found in Mongolia, NewZealand, on Youngil and Gampo in Korea, etc.

The natural zeolite is desirably a silicon zeolite-based mineral havingpositive ion surface charges, and the silicon zeolite has antibacterialactivities through positive ion exchange, thereby making it possible tohave bacteriostatic activities. Further, the silicon zeolite has strongadsorptive characteristics to thus attach underwater pollutants thereto,thereby purifying the water, and it attaches a variety of suspendedsolids in large quantities thereto to prevent the occurrence of greenand red tides.

Further, the natural zeolite serves to suppress nutritive salts andheavy metals from being dissolved from sediments, thereby preventingwater pollution.

Accordingly, the natural zeolite according to the present invention ismade by mixing clinoptilolite not heated and mordenite or illite or bymixing clinoptilolite, mordenite, and illite, and while the particlessizes of the mixture are being limited to avoid the use of sand, themixture is molded by addition of cement and water, thereby manufacturinga zeolite block for improving water quality.

The clinoptilolite may be exchanged to positive ions according toconditions to thus perform positive ion exchange with metal ions havinghigh antibacterial effectiveness, such as Ag, Cu, and Zn, therebyexhibiting high antibacterial activities stably and consistently. Themordenite is porous to exhibit high adsorption capacity, thereby beingexcellent in removing volatile organic compounds, and the illite isexcellent in heavy metal dissolution, ammonia deodorization, and thelike.

Accordingly, the natural zeolite according to the present invention ismade by mixing the clinoptilolite and the mordenite or illite or bymixing the clinoptilolite, the mordenite, and the illite, to a givenratio after they are machined to given particle sizes, and next, cementand water are addedly bonded to the zelite to thus manufacture theeco-friendly zeolite block for improving water quality.

In conclusion, the natural zeolite block according to the presentinvention is made using the characteristics of the natural zeolite andthen built in water, thereby purifying the water polluted by means ofpollutants, improving eutrophication in the water, and purifying allkinds of harmful substances and heavy metals melted in water tocontribute to water quality improvement and ecosystem restoration.

Background of the Related Art

A block for water purification is disclosed in Korean Patent No.10-1959348, which is made of a composition obtained by mixingclinoptilolite, mordenite, and bentonite, but the conventional block ismade by heating the clinoptilolite, mordenite, and bentonite to atemperature of 300 to 400° C., pulverizing them to 200 to 400 mesh, andmixing them to a given ratio, so that energy cost occurrence and carbondioxide emission may be caused and chemicals for treatment of oxidizingagents may be used, thereby failing to make an eco-friendly product.Further, the powder type particles are used, and upon molding,accordingly, sand is used as aggregate to bond the particles, so thatthe natural pores of the zeolite may be blocked by the sand to thusdecrease consistent water quality improvement capability. In addition,the manufacturing cost may be raised, and above all, the functionalityof the zeolite may be lost to thus give harms to environments.

SUMMARY OF THE INVENTION

Accordingly, the present invention has been made in view of theabove-mentioned problems occurring in the related art, and it is anobject of the present invention to provide a natural zeolite block thatis capable of being built in rivers, streams, and reservoirs havingpoint and non-point pollutant sources to purify the water polluted bypollutants, to remove the eutrophication in the water to prevent theoccurrence of green and red tides, and to consistently purify heavymetals and all kinds of harmful substances flowing into the water and toa method for manufacturing the same.

To accomplish the above-mentioned objects, according to the presentinvention, there is provided a natural zeolite block for improving waterquality, including a zeolite made by mixing clinoptilolite having theparticles of given sizes and mordenite or illite having the particles ofgiven sizes to a given ratio or by mixing clinoptilolite having theparticles of given sizes and mordenite and illite each having theparticles of given sizes to a given ratio wherein cement and water areadded to the zeolite to make a mixture, and the mixture is molded as thenatural zeolite block.

According to the present invention, desirably, the zeolite may be madeby mixing 80 to 92 wt % of the clinoptilolite and 8 to 20 wt % of themordenite with respect to the total weight of the zeolite of 100 wt %,by mixing 80 to 92 wt % of the clinoptilolite and 8 to 20 wt % of theillite with respect to the total weight of the zeolite of 100 wt %, orby mixing 80 to 90 wt % of the clinoptilolite, 5 to 10 wt % of themordenite, and 5 to 10 wt % of the illite, and 12 to 15 wt % of cementand 10 to 15 wt % of water may be added to the total weight of thecomposed zeolite to make a mixture so that the mixture is put in amolding frame to manufacture the zeolite block.

According to the present invention, desirably, the zeolite is made bypreparing 15 wt % of the clinoptilolite having the particles of sizes inthe range of 8 to 10 mm, 45 wt % of the clinoptilolite having theparticles of sizes in the range of 2.5 to 5 mm, 20 wt % of theclinoptilolite having the particles of sizes in the range of 1.2 to 2.4mm, and 20 wt % of the clinoptilolite having the particles of sizes inthe range of 0.5 to 1.2 mm.

According to the present invention, desirably, the zeolite is made bypreparing 45 wt % of the mordenite having the particles of sizes in therange of 8 to 10 mm and 55 wt % of the mordenite having the particles ofsizes in the range of 2 to 5 mm, and the illite having the particles ofsizes in the range of 0.5 to 10 mm.

According to the present invention, desirably, the shapes and sizes ofthe zeolite block according to the present invention may be shown inFIGS. 1 to 18 .

According to the present invention, desirably, the zeolite blockaccording to the present invention may have hole(s) formed on a bodythereof, an irregular main wall for expanding a surface area thereof,and concave and convex portions formed on top thereof to form a fordaccording to the flow of water.

BRIEF DESCRIPTION OF THE DRAWINGS

The above and other objects, features and advantages of the presentinvention will be apparent from the following detailed description ofthe embodiments of the invention in conjunction with the accompanyingdrawings, in which:

FIGS. 1 to 18 show a natural zeolite block with various shapes and sizesaccording to the present invention.

DETAILED DESCRIPTION OF THE EMBODIMENTS

The present invention provides a zeolite block manufactured withspecific components.

According to the present invention, a zeolite is made by mixingclinoptilolite and mordenite or illite to a given ratio or by mixingclinoptilolite, mordenite, and illite to a given ratio, and in thiscase, the mixing is performed after the particles of the minerals aremachined to given sizes. Next, the minerals are bonded by water andcement, without any sand, thereby manufacturing the zeolite blockaccording to the present invention.

With respect to the total 100 wt % of the zeolite, in specific, thezeolite is made by mixing 80 to 92 wt % of clinoptilolite having theparticles of sizes in the range of 0.5 to 10 mm and 8 to 20 wt % ofmordenite having the particles of sizes in the range of 0.5 to 10 mm, bymixing 80 to 92 wt % of clinoptilolite having the particles of sizes inthe range of 0.5 to 10 mm and 8 to 20 wt % of illite having theparticles of sizes in the range of 0.5 to 10 mm, or by mixing 80 to 90wt % of clinoptilolite, 5 to 10 wt % of mordenite, and 5 to 10 wt % ofillite, and next, 12 to 15 wt % of cement and 10 to 15 wt % of water areadded to the total weight of the zeolite composition to thus make amixture. The mixture is put into a frame and condensely molded throughvibration and compression, thereby manufacturing the natural zeoliteblock with a given shape for improving water quality.

Further, the present invention provides a method for manufacturing anatural zeolite block, including the steps of: preparing 15 wt % ofclinoptilolite having the particles of sizes in the range of 8 to 10 mm,45 wt % of clinoptilolite having the particles of sizes in the range of2.5 to 5 mm, 20 wt % of clinoptilolite having the particles of sizes inthe range of 1.2 to 2.4 mm, and 20 wt % of clinoptilolite having theparticles of sizes in the range of 0.5 to 1.2 mm; preparing 45 wt % ofmordenite having the particles of sizes in the range of 8 to 10 mm and55 wt % of mordenite having the particles of sizes in the range of 2 to5 mm; preparing illite having the particles of sizes in the range of 0.5to 10 mm; making a zeolite by selecting one method among various mixingmethods in which when the total weight of the zeolite is 100 wt %, inthe prepared materials, 80 to 92 wt % of clinoptilolite and 8 to 20 wt %of mordenite are mixed, 80 to 92 wt % of clinoptilolite and 8 to 20 wt %of illite are mixed, and 80 to 90 wt % of clinoptilolite, 5 to 10 wt %of mordenite, and 5 to 10 wt % of illite are mixed; adding 12 to 15 wt %of cement and 10 to 15 wt % of water with respect to the total weight ofthe made zeolite to make a mixture; putting the mixture in a frame witha given size disposed on a molding part of a block molding machine,applying 20 to 45 Hz vibrations to the mixture for three seconds and 50Hz vibrations to the mixture for 20 seconds to forcedly condense themixture in the frame, while applying 40 to 100 bar pressure to themixture by means of a pressure plate; applying an air pressure to anupper frame by means of an air bag as an auxiliary pressure device topressurizedly vibrate the mixture at 4 to 6 bar pressure, together withthe application of the vibrations generated from vibration motors, sothat while solidification difficulties caused by the physical propertiesof the lack of adhesion of mortar are being overcome, the naturalzeolite block is manufactured; and removing the molded block from theframe and curing the block at a temperature of 25 to 30° C. for aboutone to two days.

Further, the natural zeolite block according to the present inventionmay be made to a variety of shapes, and it may have dimensions of length500 mm x width 500 mm x depth 80 mm. However, of course, the zeoliteblock may have dimensions of length 1000 mm x width 1000 mm x depth 300mm. In case of a single small-sized block, it may have a weight of 15 to25 kg, and in case of a single medium-sized block, it may have a weightof 47 to 64 kg. In case of a single large-sized block, it may have aweight of 100 kg.

Moreover, each vibration motor used in the present invention isdesirably a bottom vibration type three phase squirrel cage vibrationmotor that is varied to the range of 500 to 3600 RPM in tuning rotationspeed of 3000 to 3600 RPM and the number of vibrations per minute of2800 to 3400 and generates power up to 350 bar. In this case, thevibration motors are disposed on the corners of the frame to constantlytune the vibration amplitudes, thereby providing the vibrations requiredfor the solidification to prevent defective products from beingmanufactured.

The zeolite block is made by bonding the filled materials through thesmallest amount of cement to achieve the solidification of the zeolite,and as sand is not added, further, the zeolite block can become aproduct with natural adsorption functions, antibacterial functions, andunderwater ecosystem conservation performance.

As described above, the natural zeolite block for improving waterquality according to the present invention is composed of the zeolitemade by mixing 80 to 92 wt % of the clinoptilolite having good positiveion exchangeability and 8 to 20 wt % of the mordenite having strongadsorption, by mixing 80 to 92 wt % of the clinoptilolite and 8 to 20 wt% of the illite having heavy metal adsorption, deodorization, anddissolution effectivenesses and ammonia deodorization effectiveness, orby mixing 80 to 90 wt % of the clinoptilolite, 5 to 10 wt % of themordenite, and 5 to 10 wt % of the illite, thereby manufacturing aproduct capable of treating pollutants, maximizing the pores of theproduct through the different particle sizes of the minerals, condenselybonding the zeolite through the cement and water upon molding, withoutusing any sand, to avoid environmental destruction caused by sandmining, and providing the natural functionality of the zeolite toachieve water quality improvement and water purification.

In addition, the natural zeolite block for improving water qualityaccording to the present invention is composed of natural minerals,without any heating, thereby minimizing environmental destruction, andmolded by putting the mixture into the molding frame through thecondensation caused by the application of the vibration and pressure,thereby forming the pores to the maximum. In this case, if the zeoliteblock is made without any use of sand, it may come into contact with thepollutants and sediments to provide antibacterial and bacteriostaticactivities and organic matter dissolution and purification activities,and accordingly, the zeolite block is more easily built than chips orpowder and has more excellent effectiveness than the chips or powder.Further, the particle sizes of the minerals are sortedly selected toexert the functionality of the zeolite, and a variety of particle sizesof the minerals are provided to ensure high strength and cohesion and amaximum number of pores. The zeolite block can be built under waterthrough various methods to provide beautiful underwater and watersideappearances and used to construct an optimized underwater structurehaving high affinity for aquatic animals and plants and their betterliving and propagation to thus contribute to consistent water qualityimprovement. In addition, the zeolite block is built on the bottom andside of a river to consistently suppress the dissolution of sedimentlayers through its own weight, thereby exerting ecosystem restorationfunctions and contributing to ecosystem restoration through economicalwater quality improvement and nature friendly activities.

While the present invention has been described with reference to theparticular illustrative embodiments, it is not to be restricted by theembodiments but only by the appended claims. It is to be appreciatedthat those skilled in the art can change or modify the embodimentswithout departing from the scope and spirit of the present invention.

What is claimed is:
 1. A natural zeolite block for improving waterquality, comprising: a clinoptilolite composition made by mixing 15 wt %of clinoptilolite having the particles of sizes in the range of 8 to 10mm, 45 wt % of clinoptilolite having the particles of sizes in the rangeof 2.5 to 5 mm, 20 wt % of clinoptilolite having the particles of sizesin the range of 1.2 to 2.4 mm, and 20 wt % of clinoptilolite having theparticles of sizes in the range of 0.5 to 1.2 mm with respect to thetotal weight of the clinoptilolite composition; a mordenite compositionmade by mixing 45 wt % of mordenite having the particles of sizes in therange of 8 to 10 mm and 55 wt % of mordenite having the particles ofsizes in the range of 2 to 5 mm with respect to the total weight of themordenite composition; and an illite composition having the particles ofsizes in the range of 0.5 to 10 mm, wherein when the total weight ofzeolite is 100 wt %, 80 to 92 wt % of the clinoptilolite composition and8 to 20 wt % of the mordenite composition are mixed, 80 to 92 wt % ofthe clinoptilolite composition and 8 to 20 wt % of the illitecomposition are mixed, or 80 to 90 wt % of the clinoptilolitecomposition, 5 to 10 wt % of the mordenite composition, and 5 to 10 wt %of the illite composition are mixed to thus make a mixture, and themixture is mixed with 12 to 15 wt % of cement and 10 to 15 wt % of waterwith respect to the total 100 wt % of the zeolite mixture and thus madeto a block body with given dimensions.